Effective inhibition of T95 steel corrosion in 15 wt% HCl solution by aspartame, potassium iodide, and sodium dodecyl sulphate mixture.

抄録

Sustainable development goal 12 advocates the production and consumption of green and sustainable commodities. As such, pressure is mounting on the oil and gas industries for a paradigm shift. This work explores the potential of aspartame (a derivative of aspartic acid and phenylalanine) based formulation as a green inhibitor. The inhibiting effect of aspartame alone and in combination with potassium iodide (KI) or sodium dodecyl sulphate (SDS) or both on T95 steel in 15 wt% HCl solution at 60-90 °C is investigated using weight loss, electrochemical, and surface analysis techniques. The results show severe metal corrosion especially at 90 °C with a corrosion rate (v) of 186.37 mm/y. Aspartame inhibits corrosion and its inhibition efficiency (η) increases with an increase in temperature. At 6.80 mM, η of 86% is obtained at 90 °C. The addition of SDS to aspartame produces an antagonistic effect. A KI-aspartame mixture produces an antagonistic effect at 60 °C and 70 °C but a synergistic effect at 80 °C and 90 °C. There is a strong synergy when aspartame (6.80 mM), KI (1 mM), and SDS (1 mM) are mixed especially at higher temperatures. The mixture reduces v from 186.37 to 14.35 mm/y, protecting the metal surface by 92% at 90 °C. The mixture can be considered an acidizing corrosion inhibitor.